Taşlıçukur Öztürk, ZeynepPehlivan, Abdullah Koray2024-06-132024-06-1320201304-2025https://search.trdizin.gov.tr/tr/yayin/detay/422527https://hdl.handle.net/11501/886In this study, GeKa Tempo B65 electrodes are used in the welding of highstrength low alloy (HSLA) S355JR steel. It is aimed to increase the impactresistance of the electrodes at minus temperatures. In order to observe themechanical properties of the materials, tensile, impact energy test andCTOD test are performed. Implicit electric arc welding is chosen as thewelding method. Electrodes with three different compositions and grainstructures are prepared for welding. Optical microscope is used to observethe surface images of the weld seams. It is observed that the grain structureof the sample, the amount of alloying elements and the heat input during thewelding of the sample significantly affect the impact resistance of thewelded samples.Bu çalışmada GeKa Tempo B65 elektrotları yüksek mukavemetli düşük alaşımlı (HSLA) S355JR çeliğinin kaynağında kullanılmıştır. Eksi sıcaklıklarda elektrotların darbe dayanımının arttırılması amaçlanmaktadır. Malzemelerin mekanik özelliklerini incelemek için çekme, çentik darbe testi ve CTOD testi yapılmıştır. Kaynak yöntemi olarak örtülü elektrik ark kaynağı seçilmiştir. Üç farklı bileşime ve tane yapısına sahip elektrotlar kaynak için hazırlanmıştır. Kaynak dikişlerinin yüzey görüntülerini gözlemlemek için optik mikroskop kullanılmıştır. Numunenin tane yapısının, alaşım elementlerinin miktarının ve numunenin kaynağı sırasındaki ısı girişinin, kaynaklı numunelerin darbe dayanımlarını önemli ölçüde etkilediği görülmüştür.eninfo:eu-repo/semantics/openAccessHigh Strength Low Alloy SteelElectrode MaterialsWeldingMechanical PropertiesMicrostructureYüksek Mukavemetli Düşük Alaşımlı ÇelikElektrot MalzemelerKaynakMekanik ÖzelliklerMikroyapıArticle192217142252716