Effect of laser welding speed on pore formation in AA 6061 T6 alloy

dc.contributor.authorGündoğdu İş, Emine
dc.contributor.authorTopuz, Polat
dc.contributor.authorAkman, Erhan
dc.contributor.authorYılmaz, Muharrem
dc.date.accessioned2024-06-13T20:18:30Z
dc.date.available2024-06-13T20:18:30Z
dc.date.issued2020
dc.departmentMeslek Yüksekokulu, Gedik Meslek Yüksekokulu, Kaynak Teknolojisi Programı
dc.description.abstractIn this study, 6 mm thick plates of Al 6061 T6 alloy are joined by laser welding at four welding speeds (40 mm x s(-1), 35 mm x s(-1), 25 mm x s(-1), and 20 mm x s(-1)). The welded joints are made using a 4000 W fiber laser welding machine. The effect of laser welding speed on the pores formed in the weld seam was investigated. In this manner, it was found that with a change in laser welding speed the amount of pores formed in the structure also changed. In addition, after the welding process, macroscopic examinations, tensile tests and the hardness tests were made. As a result of the experiments performed, it was determined that, the laser welding speed was highly effective for pore formation.
dc.identifier.doi10.3139/120.111573
dc.identifier.endpage984
dc.identifier.issn0025-5300
dc.identifier.issue10
dc.identifier.scopus2-s2.0-85093072669
dc.identifier.scopusqualityQ2
dc.identifier.startpage979
dc.identifier.urihttps://doi.org/10.3139/120.111573
dc.identifier.urihttps://hdl.handle.net/11501/1411
dc.identifier.volume62
dc.identifier.wosWOS:000580591700002
dc.identifier.wosqualityQ2
dc.indekslendigikaynakWeb of Science
dc.indekslendigikaynakScopus
dc.institutionauthorGündoğdu İş, Emine
dc.institutionauthorTopuz, Polat
dc.language.isoen
dc.publisherWalter de Gruyter GmbH
dc.relation.ispartofMaterials Testing
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/closedAccess
dc.subjectAl 6001 T6 Alloy
dc.subjectLaser Welding
dc.subjectPores
dc.subjectWelding Speed
dc.titleEffect of laser welding speed on pore formation in AA 6061 T6 alloy