Effect of welding speed and shielding gas composition on the properties of laser welded EN AW 6061-T6 al alloy using 5356 filler metal

Basit Öğe Kaydı
dc.authoridGundogdu Is, Emine/0000-0002-7614-9165
dc.authorwosidGündoğdu İş, Emine/IXD-5493-2023
dc.contributor.authorGundogdu Is, Emine
dc.contributor.authorAtapek, S. Hakan
dc.contributor.authorYilmaz, Muharrem
dc.date.accessioned2024-06-13T20:18:28Z
dc.date.available2024-06-13T20:18:28Z
dc.date.issued2023
dc.departmentİstanbul Gedik Üniversitesi
dc.description.abstractIn this study, EN AW 6061-T6 Al alloy having a thickness of 6 mm was joined with a 5000 W fiber laser welding machine using different welding speeds (20, 25, and 35 mm/s) and shielding gas compositions (100% Ar, % 50 Ar + % 50 He, % 25 Ar + 75 He). In order to reduce the strength decrease in the weld zone, 5356 filler metal with a diameter of 1.2 mm was used with the cold wire feeding method at a constant speed of 2 m/min. Structural analyses of the joints were performed by macroscopic and microscopic examination, and hardness profiles and strength values of the joints were determined by mechanical tests. The findings showed that (i) the width of the seam increased due to the increase in the amount of He in the gas composition, and the number of pores decreased accordingly, (ii) although no significant change was observed in the hardness profiles, the highest tensile strength value (242 MPa) was obtained using a gas composition of 50% He + 50% Ar and welding speed of 20 mm/s, (iii) shear failure was the dominant fracture, and the porosities played a decisive role in the fracture.
dc.identifier.doi10.2351/7.0000968
dc.identifier.issn1042-346X
dc.identifier.issn1938-1387
dc.identifier.issue3
dc.identifier.scopus2-s2.0-85163773349
dc.identifier.scopusqualityQ2
dc.identifier.urihttps://doi.org/10.2351/7.0000968
dc.identifier.urihttps://hdl.handle.net/11501/1388
dc.identifier.volume35
dc.identifier.wosWOS:001017740500001
dc.identifier.wosqualityN/A
dc.indekslendigikaynakWeb of Science
dc.indekslendigikaynakScopus
dc.language.isoen
dc.publisherAip Publishing
dc.relation.ispartofJournal of Laser Applications
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/closedAccess
dc.subjectAr-He Shielding Gas Effect
dc.subjectFiber Laser Welding
dc.subject5356 Filler Metal
dc.subjectEn Aw 6061-T6 Al Alloy
dc.subjectWelding Speed
dc.subjectMechanical-Properties
dc.subjectAluminum-Alloy
dc.subjectHeat-Treatment
dc.subjectTensile Properties
dc.subjectProcess Parameters
dc.subjectMicrostructure
dc.subjectPrecipitation
dc.subjectStrength
dc.subjectAr
dc.subjectChallenges
dc.titleEffect of welding speed and shielding gas composition on the properties of laser welded EN AW 6061-T6 al alloy using 5356 filler metal
dc.typeArticle

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu