Effect of TIG welding parameters in joining grade 2 pure titanium

Basit Öğe Kaydı
dc.contributor.authorSonmez, Murat
dc.contributor.authorTopuz, Polat
dc.date.accessioned2024-06-13T20:18:22Z
dc.date.available2024-06-13T20:18:22Z
dc.date.issued2021
dc.departmentİstanbul Gedik Üniversitesi
dc.description.abstractGrade 2, the most widely used pure titanium in the industry, has high corrosion resistance, excellent ductility, good weldability and is easily machinable. If titanium is exposed to temperatures above 500 degrees C due to moisture or hydrocarbons in the air, it is susceptible to taking up oxygen, nitrogen, carbon and hydrogen. This can cause cracks, especially after welding. Therefore, protection of the welding zone from external factors is of great importance during welding. For these reasons, TIG welding is the most widely used method for titanium welding. In this study, Grade 2 pure titanium plates are joined by TIG welding at three (40 A, 60 A and 80 A) current values under the same conditions. For the welding process, 2 wt.-% cerium addition Tungsten tip and high purity (99.99 vol.-%) argon was used as a shielding gas. After a visual inspection of the welded samples, microstructure inspections, macrostructure inspections, hardness measurements, bending tests and tensile tests were performed in accordance with the standards. As a result of the investigations, it was determined that the most suitable current value for the joining of Grade 2 titanium by TIG welding was 60 A.
dc.description.sponsorshipIstanbul Gedik University, Scientific Research Projects Coordination Department [GDK201804-05]
dc.description.sponsorshipThis research was supported by Istanbul Gedik University, Scientific Research Projects Coordination Department (Project No. GDK201804-05).
dc.identifier.doi10.1515/mt-2020-0071
dc.identifier.endpage425
dc.identifier.issn0025-5300
dc.identifier.issn2195-8572
dc.identifier.issue5
dc.identifier.startpage420
dc.identifier.urihttps://doi.org/10.1515/mt-2020-0071
dc.identifier.urihttps://hdl.handle.net/11501/1348
dc.identifier.volume63
dc.identifier.wosWOS:000672581300004
dc.identifier.wosqualityQ2
dc.indekslendigikaynakWeb of Science
dc.language.isoen
dc.publisherWalter De Gruyter Gmbh
dc.relation.ispartofMaterials Testing
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/closedAccess
dc.subjectGrade 2 Pure Titanium
dc.subjectWeldability
dc.subjectTig Welding
dc.subjectWelding Current
dc.subjectShielding Gas
dc.titleEffect of TIG welding parameters in joining grade 2 pure titanium
dc.typeArticle

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu